Nedgången av betong hänvisar främst till dess mjukdoms- och pumpbarhetsegenskaper . Faktorerna som påverkar nedgången av betong inkluderar främst förändringar i gradering, fuktinnehåll, vägning av materialavvikelse, dosering av blandningar och den lätt förbises temperaturen i cement .}
Nedgången påverkar huvudsakligen bearbetbarheten för betong, särskilt säkerställer vattenhållning, flödesbarhet och sammanhållning av betong under normal konstruktion .
Workability refers to the ability of concrete to be easily constructed and uniformly compacted, which is a comprehensive performance that includes fluidity, cohesiveness, and water retention. The impact and workability mainly include water content, water cement ratio, sand ratio, as well as cement type, aggregate conditions, time and temperature, additives, and other aspects.
The test method for slump: Use a trumpet shaped slump bucket with an upper opening of 100mm, a lower opening of 200mm, and a height of 300mm. After pouring concrete, compact it and then pull out the bucket. The concrete will collapse due to its own weight. Subtract the height of the highest point of the collapsed concrete from the height of the bucket (300 mm) För att få nedgången om skillnaden är 10 mm, är nedgången 10.
Nedgången av betong bör bestämmas baserat på konstruktionsavsnittet, stålinnehåll, transportavstånd, hällmetod, transportläge, vibrationskapacitet och klimatförhållanden för byggnaden . när man väljer blandningens proportioner bör omfattande hänsyn till och en mindre nedgång bör antas . den slumpmässiga är huvudsakligen påverkas av följande ASPELTER:
1. Effekten av betong råvaror
Due to different storage times and batches, the moisture content of Shahe washed sand is unstable, and there are limitations in determining the moisture content through experiments. Generally, the moisture content of coarse aggregates is relatively stable, but sometimes it can also change. The reason is that aggregate factories are mostly open storage, and the moisture content of aggregates changes after Rain . Olika vattenabsorptionshastigheter för aggregat under betongblandning kan orsaka varierande avvikelsegrader i betongnedgång .
2. Mekaniska och blandningstidseffekter
Long mixing time of concrete can increase the water absorption of aggregates, reduce the free moisture in concrete clinker, and cause loss of concrete slump. The measurement system error of concrete mixing machinery can also cause the loss of concrete slump. The concrete mix ratio is obtained through precise calculation and multiple trial adjustments. Any material with inaccurate Mätning kommer att orsaka en förändring i materialets specifika ytarea per enhet . ju större förändringen i materialets specifika ytarea, desto större förlust av nedgång över tid .
3. Påverkan av betongtransportmaskiner
The longer the transportation distance and time of the concrete mixer truck, the less free water in the concrete clinker due to various reasons such as chemical reactions, water evaporation, and aggregate water absorption, resulting in the loss of concrete slump over time. The concrete belt conveyor and drum can also cause mortar loss, which is also an important reason for the loss of concrete slump.
4. Påverkan av betonghällhastighet
During the concrete pouring process, the longer the concrete clinker reaches the warehouse surface, the more free water in the concrete clinker will rapidly decrease due to various reasons such as chemical reactions, water evaporation, and aggregate water absorption, resulting in slump loss. Especially when the concrete is exposed to a conveyor belt, the surface area in contact with the external environment is large, and water evaporation is rapid, which has the Största påverkan på nedgångsförlusten av betongen . Enligt faktiska mätningar, när temperaturen är cirka 25 grader, kan nedgången av betongklinker förlora upp till 4 cm inom en halvtimme .
5. Påverkan av betonghällningstid
De olika hälltiderna med betong är också ett viktigt skäl för förlusten av betongnedgång . Påverkan är relativt liten på morgonen och kvällen, men större på eftermiddagen och eftermiddagen . Temperaturen är låg på morgonen och kvällen, och avdunstningen av vatten är långsam . temperaturen är hög i eftermiddagen och eftermiddagen och eftermiddagen, och kvällen är snabb {3 {3 {}} temperaturen är hög i eftermiddagen och eftermiddagen och eftermiddagen, och den evaporation {3 {3.}) Vattenförlust, desto större förlust av betongnedgång, och desto sämre är betongens flytande och sammanhållning, vilket gör det svårt att säkerställa kvalitet